Specializing in Conveyor Belts & Timing Belts to Help Keep Your Production Running Smooth.
 |
Purpose:
White rubber conveyor belt is mainly used to transport light colored materials or finished articles with block, granular and powder shape.
Structure:
The white rubber conveyor belt is made of multi-layer impregnated nylon canvas and EP canvas as the skeleton material, with white adhesive, covered with white covering rubber, and processed by calendering, molding, vulcanization and other processes.
Features:
This product is light, clean and pollution proof
Main technical indicators:
Project | Type | ||
NN、EP | |||
Adhesion strength | Overlay and Between cores | Thickness of covering layer ＞ 1.5mm More than N/mm | 3.5 |
Thickness of covering layer: 0.8 ~ 1.5mm More than N/mm | 3.2 | ||
Between layers ≥ n / mm | 4.5 | ||
Full thickness tensile strength value of tape / N / mm | 160 ~ 3150 | ||
Elongation of full thickness longitudinal reference force of belt /% ≤ | 4 | ||
Covering compound | Breaking strength / MPa ≥ | 15 | |
Elongation at break /% ≥ | 350 | ||
Abrasion / mm3 ≤ | 250 | ||
Purpose:
White rubber conveyor belt is mainly used to transport light colored materials or finished articles with block, granular and powder shape.
Structure:
The white rubber conveyor belt is made of multi-layer impregnated nylon canvas and EP canvas as the skeleton material, with white adhesive, covered with white covering rubber, and processed by calendering, molding, vulcanization and other processes.
Features:
This product is light, clean and pollution proof
Main technical indicators:
Project | Type | ||
NN、EP | |||
Adhesion strength | Overlay and Between cores | Thickness of covering layer ＞ 1.5mm More than N/mm | 3.5 |
Thickness of covering layer: 0.8 ~ 1.5mm More than N/mm | 3.2 | ||
Between layers ≥ n / mm | 4.5 | ||
Full thickness tensile strength value of tape / N / mm | 160 ~ 3150 | ||
Elongation of full thickness longitudinal reference force of belt /% ≤ | 4 | ||
Covering compound | Breaking strength / MPa ≥ | 15 | |
Elongation at break /% ≥ | 350 | ||
Abrasion / mm3 ≤ | 250 | ||